https://www.selleckchem.com/products/3,4-dichlorophenyl-isothiocyanate.html It is imperative but challenging to develop non-noble metal-based bifunctional electrocatalysts for oxygen evolution reaction (OER) and hydrogen evolution reaction (HER). Our work reports a core-shell nanostructure that is constructed by the electrodeposition of ultrathin NiFe-LDH nanosheets (NiFe-LDHNS) on Cu2Se nanowires, which are obtained by selenizing Cu(OH)2 nanowires in situ grown on Cu foam. The obtained Cu2Se@NiFe-LDHNS electrocatalyst provides more exposed edges and catalytic active sites, thus exhibiting excellent OER and HER electrocatalytic performance in alkaline electrolytes. This catalyst needs only an overpotential of 197 mV for OER at 50 mA cm-2 and 195 mV for HER at 10 mA cm-2. Besides, when employed as a bifunctional catalyst for overall water-splitting, it requires a cell voltage of 1.67 V to reach 10 mA cm-2 in alkaline media. Furthermore, the corresponding water electrolyzer demonstrates robust durability for at least 40 h. The excellent performance of Cu2Se@NiFe-LDHNS might be ascribed to the synergistic effect from the ultrathin NiFe-LDHNS, the Cu2Se nanowires anchored on the Cu foam, and the formed core-shell nanostructure, which offers large surface area, ample active sites, and sufficient channels for gas and electrolyte diffusion. This work provides an efficient strategy for the fabrication of self-supported electrocatalysts for efficient overall water-splitting.Self-healing conductive elastomers have been widely used in smart electronic devices, such as wearable sensors. However, nano fillers hinder the flow of polymer segments, which make the development of conductive elastomer with rapid repair and high ductility a challenge. In this work, thioctic acid (TA) was grafted onto amino-modified polysiloxane (PDMS-NH2) by dehydration condensation of amino group and carboxyl group. By introducing gold nanoparticles, a dynamic network based on S-Au interaction was con