https://www.selleckchem.com/products/bi-d1870.html High hardness and corrosion resistance of SiC (silicon carbide) bulk materials have always been a difficult problem in the processing of an all-SiC piezoresistive pressure sensor. In this work, we demonstrated a SiC sealing cavity structure utilizing SiC shallow plasma-etched process (≤20 μm) and SiC-SiC room temperature bonding technology. The SiC bonding interface was closely connected, and its average tensile strength could reach 6.71 MPa. In addition, through a rapid thermal annealing (RTA) experiment of 1 min and 10 mins in N2 atmosphere of 1000 °C, it was found that Si, C and O elements at the bonding interface were diffused, while the width of the intermediate interface layer was narrowed, and the tensile strength could remain stable. This SiC sealing cavity structure has important application value in the realization of an all-SiC piezoresistive pressure sensor.There is still much controversy regarding the epidemiology of endometriosis. The objective of this work is to conduct a systematic review, and if possible, proceed with a meta-analysis of studies that have analyzed the incidence and prevalence of this condition among women in the general population. The inclusion criteria were papers published after 1997 that had reported data of the incidence or prevalence of endometriosis. The PubMed search engine was used to identify papers meeting the inclusion criteria from 1997 to 2019, with an additional manual search for the identification of potentially eligible studies. The search was limited to papers published in English. The risk of bias was assessed according to the Joanna Briggs Institute Critical Appraisal Checklist. As a result, 27 papers, which included a total of 28,660,652 women, were classified according to the type of design and sources of information in five subgroups. Pooled estimates of prevalence for studies with self-reported data were 0.05 (95% CI 0.03; 0.06), 0.01 for population-based inte