https://www.selleckchem.com/products/AT7519.html The tribological properties of Ni3Si alloy were studied at high temperatures. The effect of the addition of Ti was also analyzed. The surface composition was analyzed by Raman spectroscopy. The results showed that the friction coefficient decreased with the increasing temperature, and the wear rate changed slightly from 25 to 400 °C. However, the wear resistance of the alloys decreased sharply at 600 °C, and this was due to the decrease of the high-temperature strength and the severe oxidation of the alloys. Although the oxidation resistance of Ni3Si alloy decreased with Ti addition, the tribological property was improved by the addition of Ti. The Ni3Si alloy with 5% Ti addition had the best wear resistance at high temperatures as compared to pure Ni3Si alloy and with 10% Ti addition, and the wear rates of the alloys were in the order of magnitude of 10-5 mm3/Nm. With the increase of temperature, the wear mechanism of pure Ni3Si alloy transformed from abrasive wear to oxidation wear. As the Ti content increased, the wear mechanisms of the alloys changed from abrasive wear to fatigue wear at low temperature, and oxidation wear and fatigue wear at high temperature.Sea foam harbors a diverse range of fungal spores with biological and ecological relevance in marine environments. Fungi are known as the producers of secondary metabolites that are used in health and agricultural sectors, however the potentials of sea foam-derived fungi have remained unexplored. In this study, organic extracts of six foam-derived fungal isolates belonging to the genera Penicillium, Cladosporium, Emericellopsis and Plectosphaerella were investigated for their antimicrobial activity against plant and human pathogens and anticancer activity. In parallel, an untargeted metabolomics study using UPLC-QToF-MS/MS-based molecular networking (MN) was performed to unlock their chemical inventory. Penicillium strains were identified as the most prolific