https://www.selleckchem.com/products/anacardic-acid.html The Al70Fe12.5V12.5Ni5, Al70Fe12.5V12.5Zr5 and Al70Fe12.5V12.5Nb5 alloys were prepared via mechanical alloying. The influence of Zr, Nb or Ni addition on the glass-forming ability of Al-Fe-V amorphous alloys have been investigated. The structure of Al70Fe12.5V12.5Ni5 was amorphous and Al70Fe12.5V12.5Zr5 was not completely amorphous by transmission electron microscopy, selected area electron diffraction and differential scanning calorimetry. Different criteria were used to evaluate the influence of the addition of alloy elements on the Glass-forming ability. The Al70Fe12.5V12.5Ni5 amorphous alloys exhibits higher glass-forming ability and activation energies of crystallization. Comparison of the effective atomic size ratio and mixture enthalpy on the glass-forming ability of these amorphous alloys demonstrates that the effective atomic size ratio value becomes more significant than the values of mixture enthalpy.The primary objective of this research was to develop a finite element model specifically designed for electron beam additive manufacturing (EBAM) of Ti-6Al-4V to understand metallurgical and mechanical aspects of the process. Multiple single-layer and 10-layer build Ti-6Al-4V samples were fabricated to validate the simulation results and ensure the reliability of the developed model. Thin wall plates of 3 mm thickness were used as substrates. Thermocouple measurements were recorded to validate the simulated thermal cycles. Predicted and measured temperatures, residual stresses, and distortion profiles showed that the model is quite reliable. The thermal predictions of the model, when validated experimentally, gave a low average error of 3.7%. The model proved to be extremely successful for predicting the cooling rates, grain morphology, and the microstructure. The maximum deviations observed in the mechanical predictions of the model were as low as 100 MPa in residual stresses and 0.05 mm in distortion