https://www.selleckchem.com/products/bi-d1870.html Basalt fiber (BF) is a new anti-corrosion and environmentally friendly material, which is expected to delay the corrosion process of steel bars and improve the durability of reinforced reactive powder concrete (RPC). The electrochemical method is a nondestructive testing and real-time monitoring technique used to characterize the corrosion behaviors of steel bars embedded in concrete structures. In this paper, the electrochemical technique was employed to evaluate the corrosion of steel bars embedded in basalt fiber modified reactive powder concrete (BFRPC). Besides, crack and steel-concrete interface damage (SCID) were considered as typical factors that affect steel corrosion in concrete. Thus, both reinforced fiber-free RPC and BFRPC specimens with crack and SCID were prepared for evaluating the steel corrosion behaviors by electrochemical methods. The results revealed that both crack and SCID would aggravate the steel corrosion, and the crack was the major factor that affects the corrosion process. Moreover, the excellent compactness of BFRPC and the bridging action of BF could effectively prevent the concrete cracking and steel corrosion process of concrete. Using reinforced BFRPC instead of ordinary concrete in practical projects could greatly extend the service life of steel bars.Educational hospitalization of patients with chronic kidney disease (CKD) may slow the progression of renal dysfunction. However, the educational aspect that is more effective has not been identified to date. In this study, patients with CKD were evaluated for gustatory threshold for salty taste and received augmented salt reduction guidance under educational hospitalization at Nagasaki University Hospital from October 2016. In total, 277 eligible patients were enrolled and hospitalized from 2012 to 2019 (mean age of 69.2 years; men comprised 62.1%). We compared 141 patients (Group A) who were educated in the hospital after October 20