https://www.selleckchem.com/products/selonsertib-gs-4997.html Device performance and commercialization of organic solar cells (OSCs) are strongly influenced by the characteristics of the interface layers. Cross-linked polymer interface layers with solvent-resistant properties are very compatible with large-area solution-processing methods of OSCs and may be beneficial to the environmental stability of OSCs due to the viscoelastic and cross-linked characteristics of the cross-linked polymer. In this work, a novel cross-linkable and alcohol-soluble pyridine-incorporated polyfluorene derivative, denoted as PFOPy, is synthesized and used as a cathode interface layer (CIL) in OSCs. For PFOPy, the pendant epoxy group can be effectively cross linked through cationic polymerization under thermal treatment and the pendant pyridine group can offer good alcohol solubility. Optical absorption tests of PFOPy films before/after washing by chloroform demonstrate the excellent solvent-resistance property for the cross-linked PFOPy film. Compared with the typical ZnO CIL, the cross-link very promising CIL in OSCs. Anaemia is associated with a wide range of negative outcomes. Diagnostic blood loss (DBL) may contribute to its occurrence. We aimed to evaluate DBL and its impact on haemoglobin (HGB) concentration and developing anaemia in the intensive care unit (ICU) patients. A study group comprised of 36 adult ICU patients. DBL during 7 consecutive, post-admission days was calculated. Anaemia occurrence was assessed using the WHO thresholds. Data on HGB and haematocrit (HCT) was subjected to analysis. Upon admission, 24 (67%) patients were diagnosed with anaemia, on the eighth day 29 (80%) subjects (with 6 new cases). The median volume of blood collected was 143.15 mL (IQR 121.4-161.65) per week. No differences in DBL were found between the subjects with newly developed anaemia and their counterparts (p=0.4). The median drop of HGB (HbΔ) was 18 gL-1 (IQR 5-28) and the median drop of